Polymer | Band (cm−1) | Time of irradiation | Type of Vibration | Intensity | |
0.0 hr | 2.0 hrs | ||||
PMS | 3446 | 3446 | 3430 | C-H stretch in benzene | Decreased |
PMS | 3014 | ------ | 3014 | Increased | |
PMS | 2923 | 2924 | 2920 | (C-H), stretching vibration of benzene | Increased |
PMS | 2854 | 2854 | 2853 | C-H stretch in aldehydes | Increased |
PMS | 1889 | 1889 | 1889 | C=O stretch | Increased |
PMS | 1602 | 1602 | 1602 | C=C stretch | Decreased |
PMS | 1443 | 1443 | 1446 | C=O stretch vibrations, Carboxylic acids-dimeric forms | Increased |
PMS | 811 | 811 | 811 | Conjugated double bond | Increased |
PMS | 547 | 547 | 549 | Mono substitution of benzene ring | Decreased |
PMS/DMTa | 3729 | 3729 | ------ | C-O-C stretching vibration | Disappears |
PMS/DMTa | 3446 | 3446 | 3423 | Increased | |
PMS/DMTa | 2924 | 2924 | 2922 | (C-H), stretching vibration of benzene | Increased |
PMS/DMTa | 2852 | 2852 | 2852 | C-H stretch in aldehydes | Increased |
PMS/DMTa | 1714 | ------- | 1714 | C=O stretch, carboxylic acid | New Band |
PMS/DMTa | 1645 | 1645 | 1337 | C=C stretch | Decreased |
PMS/DMTa | 1455 | 1455 | 1453 | C=O stretch vibrations, Carboxylic acids-dimeric forms | Decreased |
PMS/DMTa | 1114 | 1114 | 1111 | Increased | |
PMS/DMTa | 830 | 830 | 830 | Conjugated double bond | Increased |
PMS/DMTa | 671 | 671 | ----- | =C-H bending | Disappear |